industrial zirconia ceramic pins tubes bushings with thread customized supplier
Zirconia Ceramic:
Zirconium oxide ceramics are white, yellow or gray when containing impurities, and generally contain HfO 2, which is not easily separated. Pure ZrO2 has three crystal states under normal pressure. The production of zirconia ceramics requires the preparation of high-purity, good dispersion properties, ultra-fine particles, narrow particle size distribution, zirconia ultrafine powder preparation methods, zirconia purification mainly chlorination and thermal decomposition, alkali metal Oxidative decomposition method, lime melting method, plasma arc method, precipitation method, colloid method, hydrolysis method, spray pyrolysis etc.
Alumina ceramic properties: High strength, high hardness, crash resistance, wear resistance, corrosion resistance, smooth surface, low thermal conductivity, nonmagnetic etc.
Data Sheet↓
Item | Unit | Typical Values |
Physical Properties |
Color | Customized |
Density | g/cm3 | 6.0 |
Zirconia Content | % | 94.4% |
Gas permeability | 0 |
Water Absorption | 0 |
Crystal Size | um | 0.5 |
Mechanical Properties |
Rockwell Hardness(45N) | R45N | 78 |
Vickers Hardness (Load 500g) | Gpa(Kg/mm²) | 11.5(1175) |
Flexural Strength(20°C) | Mpa | 800 |
Compressive Strength(20°C) | Mpa | 2000 |
Modulus of Elasticity(20°C) | Gpa | >200 |
Fracture Toughness(20°C) | MPam1/2 | 9.0 |
Thermal Properties |
Thermal Conductivity(20°C-400°C) | W(m.K) | 2.5 |
Thermal Expansion Coefficient | 10-6/°C | 9.6 |
Thermal Shock Resistance | △T°C | 250 |
Application industry: Machinery, fiber optic, knife, medical, food, petroleum etc.
Specific application: plunger, ceramic shaft, fiber optic bushing, stub, grinding, ceramic knife, ceramic slide guide, machined plunger, mobile phone shell, watch case, haircut razor blade etc.